ELECTRONIC NOSES APPLICATIONS AND TECHNOLOGIES
Anodic sulphuration of submicron-grained thin films for IR sensingMaioco, S.
Laboratorio de Películas Delgadas, FIUBA, Paseo Colón 850, (1063) Buenos Aires, Argentina
Aragón, R.
Laboratorio de Películas Delgadas, FIUBA, Paseo Colón 850, C.P. 1063 and CINSO, CITEFA-CONICET, Lasalle 4397, Villa Martelli , Buenos Aires, Argentina, Fax: +54 11 4331 0129, E-mail:smaioco@fi.uba.ar
Received November 05, 2004. In final form May 24, 2005
Abstract
Equilibrium and kinetic properties of the anodic sulphuration of magnetron
sputtered lead thin films at room temperature are reviewed. Tafel plots and
cyclic voltametry data demonstrate the existence of competing two electron
reactions. Direct anodization produces PbS of 8 nm average grain size (Scherrer),
whereas a solution-reprecipitation mechanism induces coarser deposits. PbS2
contamination can be minimized by controlling pH and the anodic potential.
Optimized working conditions were found for 0.2 M thioacetamide solutions,
at a buffered pH of 4.6 and a working potential of 0.600 V, with respect to
the Ag/AgCl reference electrode.
Resumen
Se examinaron aspectos cinéticos y de equilibrio para la reacción
de sulfuración anódica de una película de plomo obtenida
por deposición por plasma magnéticamente confinado. Los gráficos
de Tafel y voltametría cíclica indican la existencia de reacciones
bielectrónicas competitivas. La anodización directa produce PbS
de un tamaño de grano promedio de 8 nm por la ecuación de Scherrer.
Mientras que la solución-reprecipitación induce granulometría
más gruesa. La contaminación con PbS2 , puede minimizarse
por control del pH y potencial. Las condiciones operativas óptimas se
obtienen para soluciónes de tioacetamida 0,2 M, a pH = 4,6 y potencial
anódico de 0,600 V, con respecto al electrodo de referencia Ag/AgCl.
Introduction
Nanocrystalline (1-20 nm) PbS thin films find numerous opto-electronic applications.
The onset of strong quantum confinement, when grain size becomes commensurate
with the Bohr exciton, can be used to modify the semiconducting band gap. Consequently,
a wide variety of appropriate synthesis techniques [1-3] have received recent
attention. Electrochemical methods [4-6] offer the intrinsic advantages of room
temperature operation, phase selectivity by controlling the working potential
and current density to determine grain size, which are surveyed in this investigation
of anodic processes [7].
Experimental
Lead was magnetron sputtered onto 12.5 x 12.5 x 1mm plastic PTG (polyethylene
terephthalate polyester) substrates, to a piezogravimetric thickness of 80 nm.
The lead thin films were anodised in a stirred 0.2 M thioacetamide solution,
buffered to pH = 4.6 by an acetic acid-sodium acetate buffer and PbS saturated
by Pb° electrolysis, a fretted glass separated stainless steel counter-electrode,
in 1M potassium nitrate. A voltage clamp circuit controlled the working potential,
referred to a standard Ag°/AgCl electrode placed in the sample half cell
compartment. Cyclic voltametries were undertaken upon completion of electrolysis,
at 50 mV/s, initially anodic, between 0.1 and 1.0 V.
Results and discussion
The use of thioacetamide in metallic sulphide precipitation is well established.
Its hydrolysis [8] in acid media, namely:
leads to the formation of hydrogen sulphide by the dissociation:
The kinetics
of these reactions are pH dependent, which promote different precipitation mechanisms.
For instance, at pH = 4.6, the PbS rate of precipitation [9] can exceed the
rate of hydrolysis by six orders of magnitude. Further constraints arise from
complexing reactions, which are absent in the acetic–acetate buffer. Continuous
stirring was implemented for removal of soluble reaction products from the anode
surface.
Cyclic voltametries of partially sulphured lead thin films (Fig.1)
are consistent with two competing reactions. The EMF measurements of the Pb°/work
solution//Ag°/AgCl cell, on the initial solution, correspond to a Pb2+
activity of 4.14 x 10-5, which suggests the reaction
for direct anodisation, given pK1 = 6.99 and pK2 = 13.99, for the dissociation constants of SH2 [10] and Kps = 9.04 x 10-9 for PbS [10]. Lead oxidation according to
and subsequent chemical precipitation is also present, leading to micron grain deposits of PbS, filling cracks and discontinuities produced by the release of tensile stress in the films, which serve as nucleation centres, as revealed by ambient scanning electron microscopy (Fig 2 ). This coarser grained precipitate is strongly inhibited by the face down configuration of the working electrode. Direct anodisation is dependent on the presence of light, to promote carriers to the conduction band of the PbS semiconductor. In darkness, the indirect solution and reprecipitation mechanism is dominant.
Fig.1.
Cyclic voltametry of partially anodised lead film, from 0.1 to 1 V, at 50 mV/s.
Fig.
2. Ambient SEM micrograph of PbS thin film.
The oxidation reaction:
constitutes a more serious interference, because the tetragonal PbS2 [11] phase is not a direct gap semiconductor and consequently does not contribute to the electro-optic sensitivity. X-ray diffraction patterns obtained at a glancing angle of 1°, with Cu Ka radiation, demonstrate that the presence of this contaminant, prevalent at high working potentials (Fig 3,b), is minimised by operation at 0.600 V, with respect to Ag°/AgCl (Fig. 3,a), consistent with E = 0.3778V vs. SHE.
Fig.
3. XRD with a 1º glancing angle of: a) thin film anodised at 0.600
V b) thin film anodised at 0.800 V
The strong
linear character of the Tafel plot for the voltametric data (Fig.
4) corroborates that the active processes are charge transfer controlled,
consistently with their dependence on adequate illumination. The logarithmic
current / voltage slope of 2.57 V and intercept i0 = 1.41 mA correspond
to a transfer coefficient a = 0.1.
The grain size resulting from direct anodic sulphuration may be estimated from
the Scherrer equation [12], with a width at half height of the low angle X-ray
diffraction peaks, as 8 nm, for the data in Fig 3, a.
Fig.
4. Tafel plot of cyclic voltametry data
Conclusions
Anodic sulphuration of lead thin films, at a working potential of 0.600 V with
respect to Ag/AgCl, in PbS saturated thioacetamide solutions, buffered at pH
= 4.6, produces single phase, nanometric PbS thin films, suitable for electro-optic
IR detectors. Unlike cathodic deposition techniques, anodic potential control
can be implemented to create essentially single phase galena, without resorting
to post deposition treatments. Grain size is one or two orders of magnitude
finer than that obtained from chemical deposition.
References
[1] Joshi, R. K.; Kanjilal, A.; Sehgal, H. K. Applied Surface Science 2004, 221, 43-49.
[2] Nair P. K.; Nair, M. T. S.; García, V. M.; Arenas O. L.; Peña, I.; Castillo, A.; Ayala, I. T.; Gomezdaza, O.; Sánchez, A.; Campos, J.; Hu, H.; Suárez, R.; Rincón, M. R. Solar Energy Materials and Solar Cells 1998, 52, 313-344.
[3] Salim S. M.; Hamid, O. Renewable Energy 2001, 24, 575-580.
[4] Scharifker, B.; Ferreira, Z.; Mozota, J. Electrochimica Acta, 1985, 30, 5, 677-682.
[5] Torimoto T.; Takabayashi, S.; Mori, H.; Kuwabata, S. Analytical Chemistry 2002, 522, 33-39.
[6] Saloniemi, H.; Kemmell, M.; Ritala, M.; Leskelä, M. Thin Solid Film, 2001, 386, 32-40.
[7] Higgins, S. R.; Hamers, R. J. Surface Science 1995, 324, 263-281.
[8] Mane, R. S., Sankapal, B. R.; Lokhande, C. D. Materials Chemistry and Physics 2000, 64, 215-221.
[9] Swift E.; Butler, E. A Analytical Chemistry 1956, 28, N2, 146-153.
[10] Weast, R. Ed. “Handbook of Chemistry and Physics”, 67th Edition, CRC Press Inc., Boca Raton, Florida, 1986-87.
[11] Sharon, M.; Ramaiah, K. S.; Kumar, M.; Neumann-Spallart, M.; Levy-Clement. J. of Electroanalytical Chemistry 1997, 436, 49-52.
[12] Azaroff, L. “Elements of X-ray Crystallography”, Mc. Graw Hill, 1968.