Platinum monolithic catalyst for SO2 abatement in dust-free flue-gas from combustion units
E. Alvarez, J. Blanco*, J. Otero De Becerra1, J. Olivares Del Valle2 and L. Salvador2
* Instituto de Catálisis y Petroleoquímica, CSIC., Cantoblanco, 28049 Madrid, SPAIN.
1 Departamento de Combustión y Gasificación, CIEMAT, 28040, Madrid, SPAIN.
2 Departamento de Ingeniería Química y Ambiental, ESII, 41092 Sevilla, SPAIN.
Abstract A catalytic oxidation process of traces of SO2 to SO3 for the treatment of dust-free flue-gas from power stations and some special waste incinerators has been developed. The catalyst was prepared by impregnation of platinum precursors on alumina/silicates-based material. The behavior of this industrial sized honeycombtype catalyst was studied at lab and pilotplant scale. The evolution of SO2 conversion and some physico-chemical properties of the catalyst with time in operation were examined. The 7-8 wt.% of sulfate deposition on the fresh catalyst had no influence on the catalytic activity at steady state conditions. The catalyst showed SO2 to SO3 conversion value of 80-90 vol.% operating at a temperature of 450ºC and space velocities of 3000-6150 h-1 (NTP).
Keywords SO2 oxidation; Industrial size; Honeycomb-type; Dust-free gas
I. INTRODUCTION
Nowadays, one of the tasks in environmental
protection is directed towards the development
of technologies for flue-gas SOx removal,
where further reduction in its emission levels
will be required in accordance with the future
application of more stringent regulations.
Emission control techniques for the
combustion of coal and other fossil fuels have
been developed through improvements in pre,
post and in-combustion treatments. In postcombustion
methods, the most widespread
procedure uses wet lime/limestone scrubbers
and spray dryers for flue-gas desulfuration;
latterly, the catalytic oxidation of sulfur
dioxide to sulfur trioxide and further sulfuric
acid production has emerged as an alternative,
which could avoid the usual problematic
disposal of the calcium sulfates produced from
the conventional methods. In these catalytic
systems, a useful SO3 byproduct is obtained
from which various commercial products may
be marketed, such as sulfuric acid and
ammonium sulfate (Borio and Kingston.,
(1993); Blumrich and Engler, (1993)).
Obviously, catalysts produced for commercial
application should require dust-free flue-gas
conditions.
The process might also be suitable for SO2 removal from flue-gas produced by combinedcombustion
of coal and waste, such as tanned
leather residue incineration. In Spain, tanned
leather residues have been estimated as 104 T
per year produced from shoe and leather
accessories factories. The average content of
chromium is about 4 wt.% as Cr2O3 while the
sulfur content is around 2 wt.%, although this
value can widely vary depending on the tanned
leather. The chromium oxidation state in
leather is Cr (III) with very low mobility in the
environment and low toxicity for living organisms. Nevertheless, the large volume of
the leather residues is giving rise to several
problems as the storage capacities of the
deposits are reached and the weathered
chromium salts restrict dumping alternatives.
The action of water and air produces the slow
conversion of Cr (III) to Cr (VI) which could
be lixiviated and transported away from the
stored residues. The hexavalent chromium is a
common toxic pollutant in soils and waters. Its
action on human beings covers allergic contact
dermatitis and cancers. Taking into account
these considerations, incineration could be the
best solution to get rid of this waste material.
The combined-combustion of leather residues
and coal is also an interesting alternative.
In the incineration of leather residues, the
generated ashes, enriched in chromium (the
content varies between 30-60 wt.%, depending
on raw material and incineration conditions),
can be used in ceramics, including decorative
ones, to manufacture pavements and bricks,
etc. During the incineration process, additional
drawbacks arise as the leather residues contain
significant sulfur content. The addition of
limestone to retain the SO2 emissions produces
the chromium (VI) release. The total oxidation
of Cr (III) to Cr (VI) takes place if limestone is
fed into the reactor, in the range of temperature
between 450-600°C. In this case, the catalytic
oxidation of SO2 containing flue-gas and
subsequently sulfuric acid recovery might be a
suitable solution.
In dust-free flue-gas treatment, the abrasion
effect is minimized and noble-metal
impregnated catalyst is currently used in the
abatement systems (Truex et al., 1992). In the
SO2 reduction field, some reports described
noble-metal catalysts for SO2 oxidation, where
the SO3 obtained is further converted to
sulfuric acid. As an example in the DeSONOx process (Blumrich and Engel (1993); Ohlms,
1993), the previously dust cleaned flue-gas,
was passed through a precious metal
monolithic catalyst; afterwards, the SO3-rich
flue-gas was cooled and sulfuric acid (70
wt.%) condensed. In this work, short pieces of
15 cm length were manufactured and plugging
problems between layers by dust arose.
In the development of Pt-impregnated
honeycomb catalyst for SO2 oxidation, the
objective of seeking a sulfate-proof support
has given rise to a certain number of
publications and patents. For alumina, Ziolek
et al.(1996) reported that SO2 alone is
chemisorbed at 350°C. Moreover, the SO2 adsorption on alumina mainly takes place via
the hydroxyl groups, giving rise to hydrogen
sulfite species (Mohammed-Saad et al., 1995).
When O2 is present, significant quantities of
SO2 are oxidized to SO3 and subsequently
stored on the alumina. When Pt is added, the
SO2 oxidation process is catalyzed by the
noble metal and SO2/SO3 are adsorbed on
different alumina sites (Summers, 1979). Li-
Dun et al., (1991) pointed out two types of
sulfate species on the alumina having different
environments: free sulfates and sulfates
associated with the carrier.
No information about SO2/SO3 adsorption
on sepiolite or aluminium silicates behavior
has been reported.
The role of the platinum loading and
dispersion on the carrier for the SO2 oxidation
(Xue et al., 1996) has also been pointed out.
When a Pt/alumina catalyst is used, the catalytic
activity is not strongly affected by the Pt particle
size and, there is a maximum loading
percentage at which the excess of noble metal
does not enhance the performance of the
catalyst (Matsuda et al., 1982).
In this study, a Pt-impregnated on
alumina/silicates-based support catalyst has
been developed and tested both at laboratory
and pilot-plant scale. The pilot plant has been
designed to test the industrial sized catalyst at
real operational conditions in order to evaluate
the performance of the material. The evolution
of SO2 conversion and some physico-chemical
properties of both fresh and used catalyst were
examined.
II. EXPERIMENTAL SECTION
A. Catalyst Preparation
The preparation method followed four steps: the
carrier conformation, drying and calcination, Ptspecies
impregnation and subsequent reducing.
The material of the support was prepared by
mixing the corresponding quantities of three
different components: a) a boehmite with an
average particle size of 5 µm, b) a natural α-
sepiolite containing ca. 36% of impurities,
mainly other clays and calcium carbonate with
an average aggregate-size of about 11 µm, and
c) a natural high-purity aluminum silicate with
an average particle size of 9 µm. The support
composition (by weight) was 2/2/1 for alumina, α-sepiolite and aluminum silicate, respectively.
The three components of the support were
thoroughly dry mixed before adding water.
Kneading of this slurry was performed until
homogeneous dough was obtained. The material
was conformed using an industrial-scale
extruder. Parallelepiped monoliths of
10x10x100 cm external dimensions were
obtained with square cells of 4x4 mm open-cell
and 1 mm wall thickness. In the case of
operation in low-dust conditions as a result of a
malfunction of the dust collector, the 1 m length
would avoid the interlayer plugging problems,
which arise when shorter monoliths are used.
The conformed structures were dried at
110°C and calcined at 500°C for 4 hours
causing 12% shrinkage. The bulk density of
the prepared carrier was 1.3 g cm-3 and the
mechanical strength was 119 kg cm-2.
The impregnation of this support was carried
out using a 600 ppm aqueous H2Cl6Pt solution.
The impregnation process was performed
immersing one monolith each time. A movable
cage holding the material and allowing a
constant vertical motion was built. This way,
the Pt concentration inside the monolith
channels was kept constant. The average time
for each impregnation was 15 minutes. After
each impregnation process, the released liquid
volume was replaced trying to maintain the
initial Pt concentration of 600 ppm. The
evolution of Pt concentration in the solutions
was monitored by Atomic Absorption
technique. After impregnation, the monoliths
were treated in ammonia flow at 400°C for 4
hours to produce the total Pt species reduction.
XPS analysis of the prepared catalyst gave an
average percentage of 0.12 wt.% of metallic
platinum.
B. Characterization Techniques
N2 adsorption/desorption isotherms at 77 K
were determined using a Micromeritics ASAP
2300-10D. Samples of the catalyst were outgassed overnight at 140°C to a vacuum of < 10-4 torr to ensure a dry clean surface. Surface
area determinations were made by application
of the BET equation. Total pore volume was
determined using a CE Instrument Pascal
140/240 porosimeter. Samples were also dried
at 140°C overnight. The mechanical strength
of the monolithic catalyst was determined
using a Chatillon LTCM Universal Tensile
Compression and Spring Tester with a cylinder
test head of 1 mm diameter. The test head was
positioned over a channel wall and the
pressure slowly increased until rupture of the
wall was caused; the average of ten
consecutive measurements was taken to ensure
the accuracy of the result.
Thermal Gravimetric Analysis (TGA)
determination was made using a
thermobalance Perkin Elmer TGA 7 connected
to a Fisons MD 800 mass spectrometer using a
heating ramp of 10 °C min-1 within the
temperature range of 30-950°C in 20 cm3 min-1 helium flow rate.
Platinum concentration analysis was carried
using a Perkin Elmer 3030 Atomic Absorption
(AA) Spectrophotometer. Standard AA
conditions for Pt were 265.9 nm wavelength,
0.7 nm slit and air/acetylene flame.
X-Ray photoelectron spectroscopy (XPS)
analysis of Pt was carried out using a Perkin
Elmer spectrometer model Phi 5400, with a
monochromatic Mg source (1254 eV),
operating at 12 kV and 20 mA. The samples
were outgassed under a vacuum of 10-8 bar
before placing in the analysis chamber.
A Varian 3400 model Gas Chromatograph
coupled to a flame photometric detector was
used to monitor the inlet/outlet SO2 concentration in the lab-scale experiment.
The inlet/outlet SO2 and O2 measures in the
pilot plant were performed using an ESSA
ML9850 model Ultraviolet Fluorescence
analyzer.
The EPA Method (Method 8, 1990) was
selected for SO3 sampling procedure; the
collected sulfuric acid mist was measured by
the barium-thorine titration method.
III. RESULTS AND DISCUSSION
A. Lab-Scale Catalytic Activity Test
A sample from the industrial sized monolith was selected to test the catalytic performance at lab-scale conditions. The geometric dimension of the monolith piece corresponded to a 6-open-channel structure of 25 cm length. The catalytic activity measurement was carried out in a reactor working close to the isothermal axial profile, where carborundum was used to fix and isolate the catalyst. In order to avoid the entrance of SO3 to the GC, a 98 wt.% sulfuric acid trap was placed at the reactor outlet. The operation conditions are summarized in Table 1.
Table 1. Operation conditions (NTP) for the
lab-scale test. |
The SO2 conversion to SO3 increased with time in operation and reached a constant value of 90 vol.% after the first 6 hours. No deactivation of the catalyst was observed during the following 25 hours of the test, and the conversion was kept stable at the indicated value.
B. Pilot plant catalytic activity test
A scheme of the pilot plant installation is shown in Fig. 1. The main body is a catalytic reactor containing a basket with the package of honeycomb-type monoliths arranged vertically. The prismatic basket was built to provide two separate layers of 5x4 monoliths of 9.5x9.5x100 cm with a maximum catalyst load of ca. 330 liters. The dimensions of the reactor and coupling accessories to the main gas duct assured an isokinetic gas flow at the entrance of the catalytic bed. The head unit was a gas generator constituted by a gas-oil combustion chamber with a capacity of 200-500 STD m3 h-1 of simulated flue-gas in the range of 350-500ºC.
Varying the amount of carbon sulfide added
to the gas-oil as the doping agent, the desired
SO2 concentration in the flue gas was
obtained. The air supplier valve placed in the
burner controlled the variation of O2 concentration.
The catalyst placed in the prismatic holder
occupied 151 liters total volume with a crosssection
of 0.17 m2. Gas generation was about
430-470 Nm3 h-1 in order to achieve a GHSV of around 3000 h-1. The pressure drop through
the catalytic bed was in the range of 21-24 mm of H2O m-1. The main operational parameters
are summarized in Table 2.
In addition to the above-indicated
compounds, the flue gas contained CO2, CO,
NOx (ca. 300 ppm) and unburned
hydrocarbons (ca. 600 ppm).
Two glass heated lined probes were
connected upstream and downstream of the
reactor to withdraw an aliquot for the SOx analysis. The temperature was recorded at the
top and bottom of the reactor. A further
thermocouple was located at 15 cm depth
along a selected central monolith channel from
the top of the reactor.
In Fig. 2, the temperature of the
thermocouple inside the monolithic channel,
the total flow and the SO2 inlet and SO2/SO3 outlet are plotted against the time in operation.
Only data from the first 20 hours were plotted.
The reaction system reached the stationary
state after 13 hours, with SO2 to SO3 conversion values of about 80% until the run
stopped after 40 hours in operation. Stable
flow, temperature and O2 concentration values
were observed over the test.
From Fig. 2 it can be clearly seen that the
catalyst underwent a sulfating process during
the first 13 hours in operation as also observed
in the lab-scale test. After this step, the catalyst
presented stable behavior with an 80 vol.%
SO2 to SO3 conversion, lower than that
observed in the lab-scale experiment.
Textural properties comparison between the
fresh and used catalysts has been performed in
order to evaluate the effect of the SOx uptake
during the pilot plant run. The fresh catalyst
presented a BET surface area (SBET) of 159 m2 g-1 and a total pore volume (Vp) of 0.53 cm3 g-
1. After reaction, the SBET and Vp decreased to
123 m2 g-1 and 0.48 cm3 g-1, respectively. Pore
size distributions of both fresh and used
catalysts are plotted in Fig. 3.
The fresh catalyst presented a mesopores
with an average pore diameter centered at ca.
10 nm and a broad range between 15-100 nm
in the mesoporosity zone; in the macropore
range a broad peak within 0.6 and 10 µm pore
diameter would correspond to interparticulateThe fresh catalyst presented a mesopores
with an average pore diameter centered at ca.
10 nm and a broad range between 15-100 nm
in the mesoporosity zone; in the macropore
range a broad peak within 0.6 and 10 µm pore
diameter would correspond to interparticulate space. For the used catalyst, it can be seen that
pores with a diameter greater than 30 nm were
affected by the sulfate deposition. Otherwise,
sulfating process did not markedly alter the
mesopores with diameter below 30 nm
existing in the fresh catalyst. Moreover, the
slight decrease of the BET surface area values
indicated that the sulfatization was mainly
taking place in the range of meso and
macropores.
Thermal gravimetric (TG) and mass
spectrometry (MS) combined techniques were
used to monitor weight loss and gas released
with temperature. The results corresponding to
the fresh and used catalysts are shown in Fig. 4.
For the fresh catalyst the 6.3% total weight
loss between 20 and 950°C mainly
corresponded to H2O and CO2. In the used
sample, TG analysis showed between 20 and
400°C an 8% weight loss due to H2O release.
Between 500-950°C second range presented a
7.5% weight loss, which was mainly related to
the sulfite/sulfate decomposition.
With respect to the water signal, in the fresh
catalyst, different H2O or hydroxyl groups were
removed as the temperature was increased. Two
types of water molecules can be distinguished.
The absorbed water leaving the catalyst between
80-200°C and hydroxyl groups probably
coming from the alumina at 800°C.
In the used catalyst, the MS results showed
the water signal between 20-400°C. The used catalyst became more hygroscopic as a
consequence of the sulfite/sulfate groups
deposition. No water MS signal at about 800°C
was recorded, therefore, the hydroxyl groups
surface were also altered.
With respect to CO2, in the fresh catalyst, the
carbonates from sepiolite were removed
between 500 and 750°C. No CO2 in the used
sample in the range of 500-700°C was detected
and the carbonate decomposition took place at
higher temperature (700-900°C) than that in the
fresh sample. The CO2 peak in the used catalyst
started to show up when the SO2 peak reached
its maximum value. This CO2 might come from
the unreacted carbonate, which would have
been covered by the sulfate species.
With respect to the sulfate deposition, at
least two types of sulfates were removed from
the used catalyst. The SO2 starting to be
released at ca. 500°C might correspond to the
sulfates produced from the interaction between
silicates and SO3. A further SO2 peak showing
up when the temperature reached ca. 700°C
might be assigned to the aluminum sulfate
previously formed.
As the TG analysis indicated, the total
estimated amount of sulfite/sulfate uptake by
the catalyst was 7.5%. This value may be
compared with that obtained from the pilot
plant results. A simple calculation from the
SO2 inlet, SO2+SO3 outlet concentrations and
total flow data found that 6% (as SO3) would
be the amount of deposited on the catalysts.
The mechanical strength of the monolithic
catalyst was not altered by the 6-7 wt.% of
deposited sulfate, maintaining the fresh sample
value of 119 kg cm-2.
IV. CONCLUSIONS
The fresh catalyst adsorbed up to 7-8% (as
SO3) of SOx. Afterwards, a stable 90-80 vol.%
SO2 to SO3 conversion was achieved at
laboratory and pilot-plant scales respectively.
The textural characteristics were not
strongly affected by the sulfate deposition.
BET surface area and total pore volume were
not dramatically altered. Mesopores of less than 10 nm were unchanged, but the decrease
of wider mesopores and macropores was the
more significant effect.
The difference of 10 points in the
conversion value between the laboratory and
pilot-plant runs might be mainly assigned to
the presence of water vapor and unburned
hydrocarbons presenting the pilot-plant gas
stream.
The catalyst presents an acceptable catalytic
activity with no observed poisoning action by
SOx along with adequate mechanical
properties. Therefore, this feasible Ptimpregnated
monolithic catalyst based on
silicates/alumina might be applied in the SO2 emission reduction from dust-free flue-gas.
Acknowledgments
The authors are thankful to CICYT, ECSC and
CSE-ENDESA-OCICARBON for their
financial support. The authors gratefully
acknowledge the support from the ECSC
project (Nº 7220-ED/080).
We are also grateful to Dr. Yates for his
help in obtaining and discussing the textural
data and to Dr J. Pérez-Pariente and Dr.E.
Sastre for the TPD-MS analysis. Also, we wish
to thank Dr. C. Knapp for his valuable scientific
support.
REFERENCES
1. Blumrich, S. and B. Engler, "The DESONOX/
REDOX-process for flue gas cleaning", Catalysis Today 17, 301-309 (1993).
2.
Borio, D. C. and W.H. Kingston, "Efficient
and cost effective NOx and SO2 removal
from flue gas with the SNOXTM process", Processing and Utilization of High-Sulfur
Coals V, 451-465 (1993).
3.
Li-Dun, A., D. You-Quan, X. Tian-Cun, X.
Hong-Bing and L. Sheng-Li, "The
mechanism of sulfur-poisoning of
Pd(Pt)/Al2O3 catalysts and their
regeneration", Bartholomew C.H. & Butt J.
B. (eds). Catalyst Deactivation, 557-580
(1991).
4.
Matsuda, S., A. Kato, T. Mori, T. Kumagai, Y.
Hishinuma, H. Akimoto and F. Nakajima,
"Process for treating flue-gas", U.S. Patent
4,350,670, (1982).
5.
Method 8- "Determination of sulfuric acid
mist and sulfur dioxide emissions from
stationary sources", Environmental
Protection Agency. Pt. 60, App. A, Method.
8. 40 CFR Ch. I (7-1-90 Edition)(1990).
6.
Mohammed Saad, A.B., O. Saur, Y. Wang, C.P.
Tripp, B.A. Morrow and J.C. Lavalley,
"Effect of sodium on the adsorption of SO2 on Al2O3 and on its reaction with H2S", J.
Phys. Chem. 99, 4620-4625 (1995).
7.
Ohlms N., "The DESONOX process for flue
gas cleaning", Catalysis Today 16, 247-261
(1993).
8.
Summers J.C., "Reaction of sulfur oxides with
alumina and platinum/alumina", Environmental Science & Technology 13(3),
321-325 (1979).
9. Truex, T.J., R.A. Searles, D.C. Sun, "The
opportunity for new technology to
complement platinum group metal
autocatalysts", Platinum Metals Review 36(1), 2-11 (1992).
10.
Xue, E., K. Seshean and J.R.H. Ross, "Catalytic
control of diesel engine particulate emission:
studies on model reactions over a EuroPt-1
(Pt/SiO2) catalyst", Applied Catalysis B:
Environmental 11, 65-79 (1996).
11.
Ziolek, M., J. Kujawa, O. Saur, A. Aboulayt
and J.C. Lavalley, "Influence of sulfur
dioxide adsorption on the surface properties
of metal oxides", Journal of Molecular
Catalysis A: Chemical 112, 125-132
(1996).
Received: February 24, 2000.
Accepted for publication: April 26, 2000.
Recommended by Subject Editor G. Meira.