VERANES, Y. et al. Characterization of light-cured dental composites prepared from Bis-GMA/TEEDGDMA and Bis-GMA/MPS mistures. Lat. Am. appl. res. [online]. 2006, vol.36, n.1, pp.1-6. ISSN 0327-0793.
The aim of this study was to prepare light-cured dental composites and to evaluate their physical, chemical and mechanical properties. Experimental composites were prepared from 2, 2 bis [4-(2-hidroxy 3-metacriloxypropoxi) phenyl] propane (Bis-GMA), tetraethyleneglycol dimethacrylate (TEEGDMA), 3-methacryloxypropyl trimethoxysilane (MPS) and a hybrid filler consisting of quartz and colloidal silica particles (Aerosil 90). The initiation system was based on the pair Camphorquinone (CQ) / N, N dimethylaminoethylmethacrylate (DMAEMA). The experimental composites and a commercial dental composite used as reference (Charisma®) were submitted to determinations of depth of cure, water absorption and solubility, compressive and diametral tensile strengths, and elastic modulus, according to the indications of the ISO standards. The experimental resins presented adequate values for most of the analyzed properties, except for compressive strengths. In the Bis-GMA/ MPS/quartz-aerosil composite a better integration between filler and matrix was observed. The Bis-GMA/TEEGDMA/quartz-aerosil composite showed the best performance in regards to depth of cure, solubility in water, diametral tensile strength and elastic modulus. The properties of this composite were better than those of the commercial reference material, except for compressive strength.
Palabras clave : Light-Cured; Dental Composites; Depth of Cure; Absorption; Solubility; Mechanical Properties.