Resumen

URQUIA MORALES, Maria del C et al. In vitro study of microleakage of fissure sealant with different previous treatments. Acta odontol. latinoam. [online]. 2011, vol.24, n.2, pp.150-154. ISSN 1852-4834.

The purpose of this work was to evaluate microleakeage of a sealant after using three different techniques for conditioning the surface to be sealed. Twenty-four caries-free upper and lower premolars were used, which were preserved in distilled water at room temperature. The structural faults were enlarged using a cylindrical conical diamond (ISO 007). Teeth were randomly assigned into three groups of eight. Group I (control) was conditioned with 37% phosphoric acid (Vivadent) for 15 seconds after which the sealant Helioseal F (Vivadent) was applied and cured for 40 seconds. Group II was conditioned in the same way, after which one-step adhesive Te-econom (Vivadent) and the sealant were applied. Group III was conditioned using a self-etching adhesive, Go (SDI), after which the sealant was applied. Adhesive was applied according to the manufacturer’s instructions. The samples were thermocycled for 300 cycles between 5o and 55oC and immersed in a 2% methylene blue solution for 48 hs. at standardized temperature of 37oC ± 1o. Then they were rinsed with tap water and ground longitudinally in V-P direction with silica carbide rotatory disks of decreasing grit. The amount of leakage was evaluated under stereoscopic microscope at 40X magnification. The longitudinal penetration of dye into the tooth-sealant interface was scored on a scale of 0 to 3. The results were analyzed by a Kruskal-Wallis non-parametric test. In Group II, 100% of the samples showed low (50%) or no (50%) leakage. Both the other groups had a higher percentage of specimens with high leakage (scores 2 and 3) (P = 0.000). Group II had the best performance, with significant differences (P = 0.0028) compared to the other experimental groups. Marginal leakage was lowest when the tooth was conditioned with phosphoric acid and subsequent application of an adhesive, prior to sealant.

Palabras clave : Pit and fissure sealants; Dental leakeage; Dental etching.

        · resumen en Español     · texto en Inglés     · Inglés ( pdf )