Resumo

HAN, B. et al. On the impact of the stress situation on the optical properties of WSe2monolayers under high pressure. Pap. Phys. [online]. 2019, vol.11, n.1, pp.1-4. ISSN 1852-4249.

We have studied the optical properties of WSe2 monolayers (ML) by means of photolu-minescence (PL), PL excitation (PLE) and Raman scattering spectroscopy at room temperature and as a function of hydrostatic pressure up to ca. 12 GPa. For comparison, the study comprises two cases: A single WSe2 ML directly transferred onto one of the diamonds of the diamond anvil cell and a WSe2 ML encapsulated into hexagonal boron nitride (hBN) layers. The pressure dependence of the A and B exciton, as determined by PL and PLE, respectively, is very different for the case of the bare WSe2 ML and the hBN/WSe2-ML/hBN heterostructure. Whereas for the latter the A and B exciton energy increases linearly with increasing pressure at a rate of 3.5 to 3.8 meV/GPa, for the bare WSe2 ML the A and B exciton energy decreases with a coefficient of -3.1 and -1.3 meV/GPa, respectively. We interpret that this behavior is due to a different stress situation. For a single ML the stress tensor is essentially uniaxial with the compressive stress component in the direction perpendicular to the plane of the ML. In contrast, for the substantially thicker hBN/WSe2-ML/hBN heterostructure, the compression is hydrostatic. The results from an analysis of the pressure dependence of the frequency of Raman active modes comply with the interpretation of having a different stress situation in each case.

Palavras-chave : dichalcogeneides, monolayers, high pressure, Raman, photoluminescence, stress-strain tensors.

        · texto em Inglês     · Inglês ( pdf )