ZENKNER-NETO, Alfredo W et al. Bulk-fill restorative composites under simulated carious and erosive conditions. Acta odontol. latinoam. [online]. 2022, vol.35, n.2, pp.111-119.  Epub 30-Set-2022. ISSN 0326-4815.  http://dx.doi.org/10.54589/aol.35/2/111.

Acidic conditions can cause hydrolysis and accelerate degradation of resin composites (RCs). Since there are limited and controversial data on the effect of acids on bulk-fill RCs, this study assessed the surface roughness (SR) and flexural strength (FS) of these RCs under simulated carious and erosion conditions. Bars of Filtek Bulk Fill (FBF, 3M/ESPE), X-tra fil (XTF, Voco), Tetric N-Ceram Bulk Fill (TBF, Ivoclar/Vivadent), and Aura Bulk Fill (ABF, SDI) and a conventional RC [Filtek Z350XT (FZ, 3M/ESPE)] were allocated (n=15) to undergo caries or erosion conditions. The control group was kept in artificial saliva (AS). The bars were evaluated for SR change (final-baseline) and for three-point FS. Data were analyzed using ANOVA and Tukey’s test. At the baseline (p <0.001), the SR of RCs ranked as follows: (TBF = XTF) < FBF (none differed from FZ) < ABF. The interplay between RCs and conditions affected SR change (p = 0.025). While after storage in AS, there was no difference among RCs, following carious and erosive conditions, ABF showed higher SR change. For FS (p <0.001), XTF > (FBF = FZ) > (TBF = FZ) > ABF, with no difference among control, carious and erosive conditions (p = 0.148). Depending on the restorative bulk-fill RCs, carious and erosive conditions roughen the surface but do not affect the FS of these materials.

Palavras-chave : composite resins; acids; dental caries; tooth erosion.

        · resumo em Português     · texto em Inglês     · Inglês ( pdf )